HT (E.I.P.S) Carbon
Suitable for sweet wells with very low levels of H2S and CO2- The only UK manufacturer producing all of our Wirelines
in our own ISO 9001 accredited factory. - All Wirelines exceed the requirements of API 9A
- All Wirelines are 100% weld-free
- All Wirelines are supplied on painted steel reels
- All lengths are available on request
- All reels are packed with a unique protective wrap
for secure transport - Wirelines are coated in custom developed inhibitors to
further, prevent corrosion resistance - Stock held in the UK and strategic locations worldwide
Do you require more information?
To receive more specific details about our HT (E.I.P.S) Carbonproduct range please click below or call:
+44 (0)121 772 2555
| Chemical Analysis | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| C | Si | Mn | P | S | Cr | Mo | Cu | Ni | N | |
| Weight % | 0.9 Max | 0.15 – 0.35 | 0.4 – 0.7 | 0.02 Max | 0.025 Max | 0.10 – Max | 0.02 Max | 0.10 Max | 0.10 Max | 0.007 Max |
| Mechanical Properties | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| Wireline Diameter (in) | Minimum Breaking Load (lbf) | Typical Breaking Load (lbf) | Minimum UTS (N/mm²) | Typical UTS (N/mm²) | Yield Strength (0.2% of PS) | Elastic Limit | Modulus of Elasticity (N/mm²) | Recommended Safe Load | Sheave Diameter (in) | Minimum Wraps |
| 0.092″ | 1830 | 1848 | 1600 | 1820 | 80% UTS | 25% UTS | 18 X 10′ | 60% UTS | 11 | 33 |
| 0.108″ | 2490 | 2462 | 1590 | 1770 | 80% UTS | 25% UTS | 18 X 10′ | 60% UTS | 13 | 25 |
| 0.125″ | 3300 | 3523 | 1590 | 1885 | 80% UTS | 25% UTS | 18 X 10′ | 60% UTS | 15 | 23 |
| 0.140″ | 4200 | 3985 | 1570 | 1700 | 80% UTS | 25% UTS | 18 X 10′ | 60% UTS | 17 | 20 |
| 0.160″ | 5500 | 5205 | 1570 | 1700 | 80% UTS | 25% UTS | 18 X 10′ | 60% UTS | 20 | 20 |
| Physical Properties | ||||||||
|---|---|---|---|---|---|---|---|---|
| Wireline Diameter | Density (g/cm³) | Coefficient of Liner Expansion (Mm/m/°C) | Wireline Weight (lb/1000ft) | Minimum Wireline Stretch (in/100ft/100lb) | Thermal Conductivity (W/m.K) | Specific Heat (j/kg.K) | Resistivity (Ohm Cm) | Magnetic Permeability |
| 0.092″ | 7.87 | 0.11 | 22.66 | 0.70 | 50 | 532 | 17 | 2420 |
| 0.108″ | 7.87 | 0.11 | 31.23 | 0.51 | 50 | 532 | 17 | 2420 |
| 0.125″ | 7.87 | 0.11 | 41.84 | 0.38 | 50 | 532 | 17 | 2420 |
| 0.140″ | 7.87 | 0.11 | 52.41 | 0.307 | 50 | 532 | 17 | 2420 |
| 0.160″ | 7.87 | 0.11 | 68.45 | 0.236 | 50 | 532 | 17 | 2420 |
| Corrosion Resistance | |
|---|---|
| H2S + CO² | Very poor, may be used in very low H²S (1-2ppm) + CO² (2-3%) with inhibitors |
| Chloride (Brine, salt etc.) | Good – wire must be cleaned after use to prevent pitting |
| H2S + CO²‚ + Chloride | Extremely poor due to the presence of H²S + CO² |