Slick 6MO
Excellent corrosion resistance.6 Mo is an austenitic stainless steel with a high molybdenum content. Coupled with Nickel and Copper this gives the alloy a good resistance to pitting and crevice corrosion, especially in environments containing halide ions, e.g. chloride, bromide and fluoride solutions.
- UNS N08926 may offer a cost effective solution to Nickel and Titanium alloys in these environments.
- High strength compared to 316L and 317L austenitic stainless steels
- Excellent ductility and impact strength at both ambient and sub-zero temperatures
- Non-magnetic
- Higher resistance to abrasion, erosion and cavitation erosion than 316 and 317 stainless
- Listed in MR-01-75 for sour service oilfield applications
Do you require more information?
To receive more specific details about our Slick 6MO product range please click below or call:
+44 (0)121 772 2555
Chemical Analysis | ||||||||||
---|---|---|---|---|---|---|---|---|---|---|
C | Si | Mn | P | S | Cr | Mo | Cu | Ni | N | |
Weight % | 0.2 | 0.5 | 2.0 | 0.03 | 0.005 | 19.0 – 21.0 | 6.0 -7.0 | 0.7 – 1.5 | 24.0 – 26.0 | 0.12 – 0.20 |
Mechanical Properties | ||||||||||
---|---|---|---|---|---|---|---|---|---|---|
Wireline Diameter (in) | Minimum Breaking Load (lbf) | Typical Breaking Load (lbf) | Minimum UTS (N/mm²) | Typical UTS (N/mm²) | Yield Strength (0.2% of PS) | Elastic Limit | Modulus of Elasticity (N/mm²) | Recommended Safe Load | Sheave Diameter (in) | Minimum Wraps |
0.092″ | 1550 | 1670 | 1600 | 1730 | 80-90% UTS | 22 – 28% UTS | 16 X 10´ | 75% EBL* | 11 | 8 |
0.108″ | 2100 | 2185 | 1530 | 1650 | 80-90% UTS | 22 – 28% UTS | 16 X 10´ | 75% EBL* | 13 | 8 |
0.125″ | 2700 | 2760 | 1440 | 1550 | 80-90% UTS | 22 – 28% UTS | 16 X 10´ | 75% EBL* | 15 | 8 |
0.140″ | 3250 | 3350 | 1455 | 1500 | 80-90% UTS | 22 – 28% UTS | 16 X 10´ | 75% EBL* | 17 | 8 |
0.160″ | 4250 | 4350 | 1458 | 1492 | 80-90% UTS | 22 – 28% UTS | 16 X 10´ | 75% EBL* | 20 | 8 |
Physical Properties | ||||||||
---|---|---|---|---|---|---|---|---|
Wireline Diameter | Density (g/cm³) | Coefficient of Liner Expansion (Mm/m/°C) | Wireline Weight (lb/1000ft) | Minimum Wireline Stretch (in/100ft/100lb) | Thermal Conductivity (W/m.K) | Specific Heat (j/kg.K) | Resistivity (Ohm Cm) | Magnetic Permeability |
0.092″ | 8.1 | 0.15 | 23.29 | 0.79 | 12 | 415 | 96 | 1.01 |
0.108″ | 8.1 | 0.15 | 32.1 | 0.58 | 12 | 415 | 96 | 1.01 |
0.125″ | 8.1 | 0.15 | 43.0 | 0.43 | 12 | 415 | 96 | 1.01 |
0.140″ | 8.1 | 0.15 | 53.9 | 0.34 | 12 | 415 | 96 | 1.01 |
0.160″ | 8.1 | 0.15 | 69.1 | 0.26 | 12 | 415 | 96 | 1.01 |
Corrosion Resistance | |
---|---|
H²S + CO² | Excellent in all concentrations |
Chloride (Brine, salt etc.) | Excellent |
H²S + CO² + Chloride | Very good |
*EBL (Effective Breaking Load) = Actual Certified Breaking Load minus the weight of tools and minus the weight of wire off the drum.